Overview
PPS-HGR30 is a high-performance engineering thermoplastic composed of polyphenylene sulfide reinforced with 30% glass fibers. This material combines the inherent advantages of PPS - including exceptional thermal stability and chemical resistance - with enhanced mechanical properties provided by the glass fiber reinforcement. Developed as a solution for demanding industrial applications, PPS-HGR30 maintains dimensional stability across a wide temperature range (-40°C to +220°C continuous use). The glass fiber reinforcement significantly improves tensile strength and impact resistance compared to unfilled PPS, making it suitable for structural components under mechanical stress.
Physical and Chemical Properties
PPS-HGR30 exhibits outstanding thermal properties with a heat deflection temperature of 260°C at 1.82 MPa. The material retains its mechanical integrity even after prolonged exposure to high temperatures, with less than 1% weight loss after 500 hours at 200°C in air. The chemical resistance of PPS-HGR30 is exceptional, resisting most acids, bases, organic solvents, and automotive fluids. It shows no significant degradation when exposed to fuels, oils, or cleaning chemicals commonly used in industrial environments. The material also demonstrates excellent flame retardancy, typically achieving UL94 V-0 rating without additive flame retardants.
Main Applications
In the automotive industry, PPS-HGR30 is widely used for under-the-hood components such as sensor housings, fuel system parts, and transmission components due to its ability to withstand hot, chemically aggressive environments. The electrical/electronics industry utilizes this material for connectors, coil bobbins, and insulating components where high temperature stability and flame retardancy are critical. In industrial applications, PPS-HGR30 serves in pump components, valve parts, and chemical processing equipment where resistance to both mechanical stress and chemical exposure is required.
Safety and Storage
While PPS-HGR30 is generally stable at room temperature, proper handling procedures should be followed during processing. When heated above 300°C during injection molding or extrusion, adequate ventilation is necessary as thermal decomposition may release small amounts of hydrogen sulfide and other sulfur compounds. For storage, PPS-HGR30 pellets should be kept in their original packaging or sealed containers to prevent moisture absorption. Although the material is not particularly hygroscopic, prolonged exposure to humid conditions before processing may lead to surface defects in molded parts. Ideal storage conditions are below 30°C with relative humidity under 50%.
B2B Procurement Guide
When procuring PPS-HGR30, verify the glass fiber content percentage (typically 30±2%) and the fiber length distribution, as these factors significantly affect mechanical properties. Reputable suppliers should provide material datasheets with complete property profiles including tensile strength (typically 180-220 MPa), flexural modulus (approximately 12 GPa), and impact strength (usually 80-100 J/m). Consider requesting samples for your specific application testing, particularly if the material will be exposed to unusual chemical environments. For large volume purchases, inquire about batch-to-batch consistency guarantees and minimum order quantities. Lead times for specialty grades may range from 4-8 weeks depending on the supplier's inventory and production schedule.
Related Manufacturers
- 主营：塑胶粉末、(特种)工程塑料、热塑性弹性体、通用塑料
- 主营：PA6、PBT、PC、PC/ABS、PPS、TPU、TPV、ABS、PA66、POM、PPO/PPE、PMMA、ASA、PPA、EMAA、TPEE、PCTG、POE、EVA、PCT、SEBS、EAA、PEEK、PSU、PEI
- 主营：土炮机、瓶盖料、r-4-230bl、gpps-500n、耐 温pp、包装箱、洗衣机、碳纤维、电池盒、颗粒料、电水壶、聚塑料、聚丙烯、仪表壳、气动管、塑料袋、塑胶料、包装袋、淋浴罩、门把手、件轴承、pvc颗粒、塑料箱、电池壳、开口剂